JLS-FR105T is halogen-free, low smoke, flame retardant, irradiated cross-linkable, low toxicity, low causticity cable compound. It is applicable to automobile high-voltage wire, TV high-voltage wire, etc. It maintains excellent self-extinguish property, well protection to insulation, high flame retardancy, outstanding electrical properties, and good appearance. It can be colored directly or by mixing with Polyolefin colour masterbatch.
Property Parameter
Item
Unit
Typical Value
Test Method
Density
g/cm 3
1.19
ISO1183
Melt Flow Index
g/10min
0.80
ISO1113
HCI generation
%
0
IEC 60754-1
Toxicity Index
2.1
NES 713
LOI
%
44
ISO4589
Conductivity
μS/mm
3.6
IEC 60754-2
20°C volume resistivity
Ω·cm
2×10 13
IEC60502
PH value
6.5
IEC 60754-1
Original Tensile Strength
MPa
16
IEC60811
Original Elongation
%
350
IEC60811
Heat Aging Method
°C ×h
136 °C ×168h
IEC60811
Change of Tensile Strength
%
13
IEC60811
Change of Elongation
%
16
IEC60811
Cold Brittleness （ -25°C ）
Pass
ISO 974
Heat Extension
（200°C×15min 20N/cm2）
Loading Extension
%
81
IEC60811
Permanent deformation
%
2
IEC60811
Flame Retardancy
VW-1 FT1
UL1581
Processing Guide
1)Processing Temperature
The recommended temperature range is 180°C-190°C
°C
190
185
180
175
Barrel 1
Barrel 2
Barrel 3
Barrel 4
Barrel 5
Die
2)Extrusion Equipment
It can be processed in ordinary PVC processing machine. NO special screw is required. All kinds of screw combination and tooling are applicable.
Storage and Packaging
Store in dry place at ambient temperature. Avoid direct exposure to sunlight ,moisture and weathering.If pre-dry is required, place under 80°C for 2-4 hours. Use as soon as possible after open. Recommend storage period not more than 6 months. Standard packing of 25kg net in multi-layer bags (with PE bag inside). Customized package is also available.