	JLS- FR125		125°C Irradiated Cross-linkable Compound

	Application

JLS-FR125 is halogen free, low smoke, flame retardant, irradiated cross-linkable, low toxicity, low causticity cable compound for cable insulation/ jacket. With its excellent mechanical properties, flame retardancy and processing properties, it is applicable to automobile, electronic and electrical appliances, etc. It can be colored directly or by mixing with Polyolefin colour masterbatch.


	Property Parameter

Item		Unit	Typical Value	Test Method
Density		g/cm ³	1.14	ISO1183D
Melt Flow Index		g/10min	0.86	ISO1113
HCI generation		%	0	IEC 60754-1
Toxicity Index			3.8	NES 713
LOI		%	42	ISO4589
Conductivity		μS/mm	2.6	IEC 60754-2
20°C Volume Resistivity		Ω·cm	3.82×10 ¹²	IEC60502
pH value			6.9	IEC 60754-1
Smoke Density	Non-Flaming mode	%	53	ASTM E662
Smoke Density	Flaming mode	%	87	ASTM E662
Original Tensile Strength		MPa	16	IEC60811
Original Elongation		%	450	IEC60811
Heat Aging Method		°C × h	150 °C ×168h	IEC60811
Change of Tensile Strength		%	13	IEC60811
Change of Elongation		%	15	IEC60811
Heat Deformation		%	13	IEC60811
Cold Brittleness（-25°C）			Pass	ISO 974
Flame Retardancy		VW-1 FT1		UL1581

	Processing Guide

	1) Processing Temperature
	The recommended temperature range is 180°C-190°C

°C

190

185

180

175

Barrel 1

Barrel 2

Barrel 3

Barrel 4

Barrel 5

Die


	2) Extrusion Equipment
	It can be processed in ordinary PVC processing machine. NO special screw is required. All kinds of screw combination and tooling are applicable.

	Storage and Packaging

	Store in dry place at ambient temperature. Avoid direct exposure to sunlight, moisture and weathering. If pre-dry is required, place under 80°C for 2-4 hours. Use as soon as possible after open. Recommend storage period not more than 6 months. Standard packing of 25kg net in multi-layer bags(with PE bag inside). Customized package is also available.